Durethan® ECOBKV15H2.0
15% Glass Reinforced, Injection Molding, Heat Stabilized, Recycled Content
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Sustainability
Mass balanced, Recycled based
Mass balanced, Recycled based
Special features
- Contains recycled content
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
Yellow Card
Processing technology
Injection Molding
Injection Molding
Mechanical properties
Tensile modulus
6000
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
6140
MPa
ISO 527-1/-2
Tensile modulus (40°C)
4960
MPa
ISO 527-1/-2
Tensile modulus (100°C)
2180
MPa
ISO 527-1/-2
Tensile modulus (120°C)
2060
MPa
ISO 527-1/-2
Tensile modulus (140°C)
1950
MPa
ISO 527-1/-2
Tensile modulus (160°C)
1870
MPa
ISO 527-1/-2
Tensile modulus (180°C)
1650
MPa
ISO 527-1/-2
Tensile modulus (200°C)
1370
MPa
ISO 527-1/-2
Stress at break
125
MPa
ISO 527-1/-2
Strain at break
2.5
%
ISO 527-1/-2
Flexural modulus
4700
MPa
ISO 178
Flexural strength
180
MPa
ISO 178
Charpy impact strength (+23°C)
50
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
40
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
<10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod notched impact strength (-40°C)
<10
kJ/m²
ISO 180/1A
Puncture - maximum force (+23°C)
613
N
ISO 6603-2
Puncture - maximum force (-30°C)
608
N
ISO 6603-2
Puncture energy (+23°C)
1.8
J
ISO 6603-2
Puncture energy (-30°C)
1.8
J
ISO 6603-2
Thermal properties
Melting temperature (10°C/min)
213
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
190
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
210
°C
ISO 75-1/-2
Temp. of deflection under load (8.00 MPa)
60
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
1.1
E-4/°C
ISO 11359-1/-2
Burning Behav. at 0.75 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Oxygen index
22
%
ISO 4589-1/-2
Glow Wire Flammability Index GWFI
650
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
2
mm
IEC 60695-2-12
Electrical properties
Comparative tracking index
375
V
IEC 60112
Other properties
Water absorption
8.5
%
Sim. to ISO 62
Humidity absorption
2.6
%
Sim. to ISO 62
Density
1230
kg/m³
ISO 1183
Material specific properties
Viscosity number
138
cm³/g
ISO 307, 1157, 1628
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
260-290
°C
Mold temperature
80-100
°C