Durethan® ECOAKV30HRH2.0
30% Glass Reinforced, Injection Molding, Heat Stabilized, Hydrolysis resistant, Recycled Content
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Sustainability
Mass balanced, Recycled based
Mass balanced, Recycled based
Special features
- Contains recycled content
- Heat stabilized
- Hydrolysis resistant or enhanced hydrolytic stability
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.44
%
ISO 294-4
Molding shrinkage (normal)
0.94
%
ISO 294-4
Mechanical properties
Tensile modulus
9700
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
10300
MPa
ISO 527-1/-2
Tensile modulus (40°C)
9270
MPa
ISO 527-1/-2
Tensile modulus (100°C)
4850
MPa
ISO 527-1/-2
Tensile modulus (120°C)
4450
MPa
ISO 527-1/-2
Tensile modulus (140°C)
4140
MPa
ISO 527-1/-2
Tensile modulus (160°C)
3940
MPa
ISO 527-1/-2
Tensile modulus (180°C)
3780
MPa
ISO 527-1/-2
Tensile modulus (200°C)
3620
MPa
ISO 527-1/-2
Stress at break
180
MPa
ISO 527-1/-2
Strain at break
3.5
%
ISO 527-1/-2
Flexural modulus
9300
MPa
ISO 178
Flexural strength
280
MPa
ISO 178
Charpy impact strength (+23°C)
75
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
65
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod notched impact strength (-40°C)
<10
kJ/m²
ISO 180/1A
Puncture - maximum force (+23°C)
896
N
ISO 6603-2
Puncture - maximum force (-30°C)
776
N
ISO 6603-2
Puncture energy (+23°C)
3.1
J
ISO 6603-2
Puncture energy (-30°C)
1.9
J
ISO 6603-2
Thermal properties
Melting temperature (10°C/min)
262
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
245
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
250
°C
ISO 75-1/-2
Temp. of deflection under load (8.00 MPa)
125
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.9
E-4/°C
ISO 11359-1/-2
Burning Behav. at 0.75 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Oxygen index
26
%
ISO 4589-1/-2
Glow Wire Flammability Index GWFI
650
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
2
mm
IEC 60695-2-12
Electrical properties
Relative permittivity (100Hz)
4
-
IEC 62631-2-1
Relative permittivity (1 MHz)
3.6
-
IEC 62631-2-1
Dissipation factor (100 Hz)
80
E-4
IEC 62631-2-1
Dissipation factor (1 MHz)
160
E-4
IEC 62631-2-1
Volume resistivity
1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
Ohm
IEC 62631-3-2
Electric strength
35
kV/mm
IEC 60243-1
Comparative tracking index
450
V
IEC 60112
Other properties
Water absorption
5.5
%
Sim. to ISO 62
Humidity absorption
2
%
Sim. to ISO 62
Density
1360
kg/m³
ISO 1183
Material specific properties
Viscosity number
153
cm³/g
ISO 307, 1157, 1628
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
280-300
°C
Mold temperature
80-120
°C