Durethan® DPBM65XFM30
65% Glass/Mineral Reinforced, Injection Molding, Flame Retardant (halogen free), Heat Stabilized, Improved flow
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
- Good or high flow
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.4
%
ISO 294-4
Molding shrinkage (normal)
0.5
%
ISO 294-4
Mechanical properties
Tensile modulus
12100
MPa
ISO 527-1/-2
Stress at break
120
MPa
ISO 527-1/-2
Strain at break
1.6
%
ISO 527-1/-2
Flexural modulus
12300
MPa
ISO 178
Flexural strength
175
MPa
ISO 178
Charpy impact strength (+23°C)
30
kJ/m²
ISO 179/1eU
Izod notched impact strength (+23°C)
<10
kJ/m²
ISO 180/1A
Thermal properties
Melting temperature (10°C/min)
220
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
181
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
200
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.5
E-4/°C
ISO 11359-1/-2
Thermal conductivity in plane
1.1
W/(m K)
ASTM E1461
Thermal conductivity through plane
0.9
W/(m K)
ASTM E1461
Burning Behav. at 0.75 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
5VA
mm
IEC 60695-11-10
Burning Behav. 5V at thickness h
5VA
class
IEC 60695-11-20
Thickness tested
3
mm
IEC 60695-11-20
Oxygen index
49.1
%
ISO 4589-1/-2
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
0.75
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
775
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
0.75
mm
IEC 60695-2-13
Electrical properties
Electric strength
26.3
kV/mm
IEC 60243-1
Comparative tracking index
600
V
IEC 60112
Other properties
Water absorption
3.5
%
Sim. to ISO 62
Humidity absorption
1.2
%
Sim. to ISO 62
Density
1690
kg/m³
ISO 1183
Material specific properties
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.07
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
250-280
°C
Mold temperature
80-100
°C