Durethan® DPAKV30HREF
30% Glass Reinforced, Injection Molding, Heat Stabilized, Hydrolysis resistant, Improved flow
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
- Good or high flow
- Heat stabilized
- Hydrolysis resistant or enhanced hydrolytic stability
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.37
%
ISO 294-4
Molding shrinkage (normal)
0.82
%
ISO 294-4
Mechanical properties
Tensile modulus
8200
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
9830
MPa
ISO 527-1/-2
Tensile modulus (40°C)
8500
MPa
ISO 527-1/-2
Tensile modulus (100°C)
4460
MPa
ISO 527-1/-2
Tensile modulus (120°C)
4080
MPa
ISO 527-1/-2
Tensile modulus (140°C)
3860
MPa
ISO 527-1/-2
Tensile modulus (160°C)
3670
MPa
ISO 527-1/-2
Tensile modulus (180°C)
3500
MPa
ISO 527-1/-2
Tensile modulus (200°C)
3420
MPa
ISO 527-1/-2
Stress at break
150
MPa
ISO 527-1/-2
Strain at break
3.6
%
ISO 527-1/-2
Flexural modulus
8100
MPa
ISO 178
Flexural strength
240
MPa
ISO 178
Charpy impact strength (+23°C)
80
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
70
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
10
kJ/m²
ISO 180/1A
Puncture - maximum force (+23°C)
774
N
ISO 6603-2
Puncture - maximum force (-30°C)
756
N
ISO 6603-2
Puncture energy (+23°C)
2.7
J
ISO 6603-2
Puncture energy (-30°C)
2.5
J
ISO 6603-2
Thermal properties
Melting temperature (10°C/min)
263
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
240
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
250
°C
ISO 75-1/-2
Other properties
Density
1320
kg/m³
ISO 1183
Material specific properties
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
280-300
°C
Mold temperature
80-120
°C