Durethan® BKV320ZH2.0
20% Glass Reinforced, Blow Molding Grade, Heat Stabilized, Improved Impact
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Processing technology
Blow Molding
Blow Molding
Rheological properties
Molding shrinkage (parallel)
0.8
%
ISO 294-4
Molding shrinkage (normal)
0.6
%
ISO 294-4
Mechanical properties
Tensile modulus
6500
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
6880
MPa
ISO 527-1/-2
Tensile modulus (40°C)
5250
MPa
ISO 527-1/-2
Tensile modulus (100°C)
2270
MPa
ISO 527-1/-2
Tensile modulus (120°C)
2150
MPa
ISO 527-1/-2
Tensile modulus (140°C)
2030
MPa
ISO 527-1/-2
Tensile modulus (160°C)
1910
MPa
ISO 527-1/-2
Tensile modulus (180°C)
1770
MPa
ISO 527-1/-2
Tensile modulus (200°C)
1540
MPa
ISO 527-1/-2
Stress at break
120
MPa
ISO 527-1/-2
Strain at break
4.5
%
ISO 527-1/-2
Flexural modulus
5800
MPa
ISO 178
Flexural strength
190
MPa
ISO 178
Charpy impact strength (+23°C)
85
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
90
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
20
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
10
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
20
kJ/m²
ISO 180/1A
Thermal properties
Melting temperature (10°C/min)
221
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
191
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
212
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
1.5
E-4/°C
ISO 11359-1/-2
Other properties
Density
1240
kg/m³
ISO 1183
Material specific properties
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-120
°C