Durethan® BKV30H2.0LT

30% Glass Reinforced, Injection Molding, Heat Stabilized, Laser Transparent Black

Back to results

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Mechanical properties

Tensile modulus
9500
MPa
Stress at break
170
MPa
Strain at break
3
%
Flexural modulus
8300
MPa
Flexural strength
270
MPa
Charpy impact strength (+23°C)
80
kJ/m²
Charpy impact strength (-30°C)
70
kJ/m²
Charpy notched impact strength (+23°C)
10
kJ/m²
Charpy notched impact strength (-30°C)
<10
kJ/m²
Puncture energy (+23°C)
6
J
Puncture energy (-30°C)
4
J

Thermal properties

Melting temperature (10°C/min)
222
°C
Temp. of deflection under load (1.80 MPa)
200
°C
Temp. of deflection under load (0.45 MPa)
215
°C
Temp. of deflection under load (8.00 MPa)
110
°C
Coeff. of linear therm. expansion (parallel)
0.2
E-4/°C
Coeff. of linear therm. expansion (normal)
0.8
E-4/°C
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
Oxygen index
22
%

Electrical properties

Relative permittivity (100Hz)
4.2
-
Relative permittivity (1 MHz)
3.8
-
Dissipation factor (100 Hz)
100
E-4
Dissipation factor (1 MHz)
170
E-4
Volume resistivity
1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
40
kV/mm
Comparative tracking index
425
V

Other properties

Water absorption
7
%
Humidity absorption
2.1
%
Density
1360
kg/m³

Material specific properties

Viscosity number
140
cm³/g
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-120
°C