Durethan® BKV215W1

15% Glass Reinforced, Injection Molding, Improved Impact

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
Regulatory Affairs
Processing technology
Injection Molding

Rheological properties

Molding shrinkage (parallel)
0.5
%
Molding shrinkage (normal)
0.6
%

Mechanical properties

Tensile modulus
4400
MPa
Stress at break
85
MPa
Strain at break
4.7
%
Flexural modulus
3900
MPa
Flexural strength
135
MPa
Charpy impact strength (+23°C)
65
kJ/m²
Charpy impact strength (-30°C)
80
kJ/m²
Izod notched impact strength (+23°C)
20
kJ/m²
Puncture - maximum force (+23°C)
1760
N
Puncture - maximum force (-30°C)
785
N
Puncture energy (+23°C)
7.3
J
Puncture energy (-30°C)
3.1
J

Thermal properties

Melting temperature (10°C/min)
214
°C
Temp. of deflection under load (1.80 MPa)
180
°C
Temp. of deflection under load (0.45 MPa)
205
°C
Temp. of deflection under load (8.00 MPa)
60
°C
Coeff. of linear therm. expansion (parallel)
0.5
E-4/°C
Coeff. of linear therm. expansion (normal)
1.6
E-4/°C

Electrical properties

Comparative tracking index
600
V

Other properties

Density
1180
kg/m³

Material specific properties

Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
Melt temperature (Tmin - Tmax)
260-290
°C
Mold temperature
80-100
°C