Durethan® BKV130H3.0 DUS008

30% Glass Reinforced, Injection Molding, Heat Stabilized, Improved Impact

Back to results

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Mechanical properties

Tensile modulus
9000
MPa
Stress at break
160
MPa
Strain at break
4
%
Flexural modulus
8000
MPa
Flexural strength
250
MPa
Charpy impact strength (+23°C)
95
kJ/m²
Charpy impact strength (-30°C)
80
kJ/m²
Charpy notched impact strength (+23°C)
18
kJ/m²
Charpy notched impact strength (-30°C)
10
kJ/m²

Thermal properties

Melting temperature (10°C/min)
222
°C
Temp. of deflection under load (1.80 MPa)
205
°C
Temp. of deflection under load (0.45 MPa)
220
°C

Other properties

Density
1370
kg/m³

Material specific properties

Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
Melt temperature (Tmin - Tmax)
260-290
°C
Mold temperature
80-100
°C