Durethan® BG30X
30% Glass Fiber/Glass Beads, Injection Molding, Low Warpage
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
- Low warpage
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.48
%
ISO 294-4
Molding shrinkage (normal)
0.77
%
ISO 294-4
Mechanical properties
Tensile modulus
6300
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
6610
MPa
ISO 527-1/-2
Tensile modulus (40°C)
5350
MPa
ISO 527-1/-2
Tensile modulus (100°C)
1960
MPa
ISO 527-1/-2
Tensile modulus (120°C)
1860
MPa
ISO 527-1/-2
Tensile modulus (140°C)
1760
MPa
ISO 527-1/-2
Tensile modulus (160°C)
1820
MPa
ISO 527-1/-2
Tensile modulus (180°C)
1670
MPa
ISO 527-1/-2
Tensile modulus (200°C)
1500
MPa
ISO 527-1/-2
Stress at break
125
MPa
ISO 527-1/-2
Strain at break
4
%
ISO 527-1/-2
Flexural modulus
5800
MPa
ISO 178
Flexural strength
185
MPa
ISO 178
Charpy impact strength (+23°C)
45
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
40
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
<10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod notched impact strength (-40°C)
<10
kJ/m²
ISO 180/1A
Puncture - maximum force (+23°C)
700
N
ISO 6603-2
Puncture - maximum force (-30°C)
690
N
ISO 6603-2
Puncture energy (+23°C)
2
J
ISO 6603-2
Puncture energy (-30°C)
1.7
J
ISO 6603-2
Thermal properties
Melting temperature (10°C/min)
222
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
190
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
210
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.9
E-4/°C
ISO 11359-1/-2
Burning Behav. at 0.75 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Oxygen index
23
%
ISO 4589-1/-2
Glow Wire Flammability Index GWFI
650
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
2
mm
IEC 60695-2-12
Electrical properties
Relative permittivity (100Hz)
4.5
-
IEC 62631-2-1
Relative permittivity (1 MHz)
4
-
IEC 62631-2-1
Dissipation factor (100 Hz)
130
E-4
IEC 62631-2-1
Dissipation factor (1 MHz)
180
E-4
IEC 62631-2-1
Volume resistivity
1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
Ohm
IEC 62631-3-2
Electric strength
36
kV/mm
IEC 60243-1
Comparative tracking index
400
V
IEC 60112
Other properties
Water absorption
7
%
Sim. to ISO 62
Humidity absorption
2.2
%
Sim. to ISO 62
Density
1350
kg/m³
ISO 1183
Material specific properties
Viscosity number
140
cm³/g
ISO 307, 1157, 1628
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-120
°C