Durethan® B40FAM

Unreinforced, Injection Molding, Film Extrusion, Extrusion, Food Contact Quality, High Viscosity

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
Regulatory Affairs
Processing technology
Extrusion, Injection Molding

Mechanical properties

Tensile modulus
2800
MPa
Yield stress
75
MPa
Yield strain
4
%
Nominal strain at break
20
%
Flexural modulus
2600
MPa
Charpy impact strength (+23°C)
N
kJ/m²
Charpy impact strength (-30°C)
N
kJ/m²
Charpy notched impact strength (+23°C)
5
kJ/m²
Charpy notched impact strength (-30°C)
5
kJ/m²

Thermal properties

Melting temperature (10°C/min)
222
°C
Temp. of deflection under load (1.80 MPa)
50
°C
Temp. of deflection under load (0.45 MPa)
150
°C
Temp. of deflection under load (8.00 MPa)
40
°C
Coeff. of linear therm. expansion (parallel)
0.8
E-4/°C
Coeff. of linear therm. expansion (normal)
0.8
E-4/°C
Burning Behav. at 0.75 mm nom. thickn.
HB
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
Oxygen index
24
%

Electrical properties

Relative permittivity (100Hz)
3.9
-
Relative permittivity (1 MHz)
3.5
-
Volume resistivity
1E12
Ohm*m
Surface resistivity
Ohm
Electric strength
30
kV/mm
Comparative tracking index
600
V

Other properties

Water absorption
10
%
Humidity absorption
3
%
Density
1140
kg/m³

Material specific properties

Viscosity number
225
cm³/g
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h