Durethan® AKV35XTS1
35% Glass Reinforced, Injection Molding, Heat Stabilized
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.35
%
ISO 294-4
Molding shrinkage (normal)
0.9
%
ISO 294-4
Mechanical properties
Tensile modulus
10700
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
12100
MPa
ISO 527-1/-2
Tensile modulus (40°C)
9940
MPa
ISO 527-1/-2
Tensile modulus (100°C)
5550
MPa
ISO 527-1/-2
Tensile modulus (120°C)
5130
MPa
ISO 527-1/-2
Tensile modulus (140°C)
4740
MPa
ISO 527-1/-2
Tensile modulus (160°C)
4460
MPa
ISO 527-1/-2
Tensile modulus (180°C)
4230
MPa
ISO 527-1/-2
Tensile modulus (200°C)
4080
MPa
ISO 527-1/-2
Stress at break
185
MPa
ISO 527-1/-2
Strain at break
3.2
%
ISO 527-1/-2
Flexural modulus
10100
MPa
ISO 178
Flexural strength
280
MPa
ISO 178
Charpy impact strength (+23°C)
75
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
10
kJ/m²
ISO 180/1A
Thermal properties
Melting temperature (10°C/min)
261
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
235
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
250
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.2
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.95
E-4/°C
ISO 11359-1/-2
Other properties
Density
1410
kg/m³
ISO 1183
Material specific properties
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
270-290
°C
Mold temperature
80-120
°C
admissible residence time at Tmax
<5
min