Durethan® AKV35CXH2.0

35% Glass Fiber Reinforced, Injection Molding, Foam Applications, Heat Stabilized

Back to results

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2025-11-21
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals and F-gasses2025-02-06
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2025-04-14
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2025-10-21
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Compliance Statement Sanctions and Embargos2025-11-24
  • Conflict minerals declaration (EICC, GeSI)2025-10-21
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2025-11-03
  • EMRT Statement2025-05-27
  • Micro Plastics Statement2025-09-22
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste (EU) 2025/40 and CONEG declaration2025-06-24
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2025-11-06
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
0.3
%
Molding shrinkage (normal)
0.9
%

Mechanical properties

Tensile modulus
11500
MPa
Tensile modulus (-40°C)
12000
MPa
Tensile modulus (40°C)
10000
MPa
Tensile modulus (100°C)
5700
MPa
Tensile modulus (120°C)
5350
MPa
Tensile modulus (140°C)
5000
MPa
Tensile modulus (150°C)
4800
MPa
Tensile modulus (160°C)
4600
MPa
Tensile modulus (180°C)
4200
MPa
Tensile modulus (200°C)
3850
MPa
Stress at break
205
MPa
Stress at break (-40°C)
270
MPa
Stress at break (100°C)
120
MPa
Stress at break (120°C)
111
MPa
Stress at break (140°C)
101
MPa
Stress at break (150°C)
98
MPa
Stress at break (160°C)
94
MPa
Stress at break (180°C)
85
MPa
Stress at break (200°C)
76
MPa
Strain at break
3.5
%
Strain at break (-40°C)
3.3
%
Strain at break (120°C)
7.2
%
Strain at break (140°C)
7.5
%
Strain at break (150°C)
8.1
%
Strain at break (160°C)
8.3
%
Strain at break (180°C)
8.7
%
Strain at break (200°C)
200
%
Flexural modulus
10500
MPa
Flexural modulus (120°C)
5000
MPa
Flexural modulus (160°C)
4500
MPa
Flexural strength
310
MPa
Flexural strength (120°C)
145
MPa
Flexural strength (160°C)
120
MPa
Charpy impact strength (+23°C)
90
kJ/m²
Charpy impact strength (-30°C)
75
kJ/m²
Charpy notched impact strength (+23°C)
13.5
kJ/m²
Charpy notched impact strength (-30°C)
11
kJ/m²
Izod notched impact strength (+23°C)
12
kJ/m²
Puncture - maximum force (+23°C)
900
N
Puncture - maximum force (-30°C)
830
N
Puncture energy (+23°C)
3.2
J
Puncture energy (-30°C)
2.6
J
Weldline strength at thickness 1
100
MPa
Weldline strain at thickness 1
1.3
%
Thickness tested (1)
4
mm

Thermal properties

Melting temperature (10°C/min)
260
°C
Temp. of deflection under load (1.80 MPa)
250
°C
Temp. of deflection under load (0.45 MPa)
250
°C
Coeff. of linear therm. expansion (parallel)
0.2
E-4/°C
Coeff. of linear therm. expansion (normal)
1
E-4/°C

Electrical properties

Relative permittivity (100Hz)
4
-
Relative permittivity (1 MHz)
3.6
-
Dissipation factor (100 Hz)
50
E-4
Dissipation factor (1 MHz)
140
E-4
Volume resistivity
1E12
Ohm*m
Surface resistivity
Ohm
Electric strength
35
kV/mm
Comparative tracking index
500
V

Other properties

Water absorption
5
%
Humidity absorption
1.6
%
Density
1410
kg/m³

Material specific properties

Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.02-0.07
%
Melt temperature (Tmin - Tmax)
280-300
°C
Mold temperature
80-120
°C