Durethan® AKV30GITH2.0
30% Glass Reinforced, Injection Molding, Heat Stabilized, Excellent Surface Properties
General Information
Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
- Good surface properties
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- REACH Registration Statement2024-03-27
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-06-27
Processing technology
Injection Molding
Injection Molding
Mechanical properties
Tensile modulus
9200
MPa
ISO 527-1/-2
Tensile modulus (-40°C)
9940
MPa
ISO 527-1/-2
Tensile modulus (40°C)
9370
MPa
ISO 527-1/-2
Tensile modulus (100°C)
3860
MPa
ISO 527-1/-2
Tensile modulus (120°C)
3610
MPa
ISO 527-1/-2
Tensile modulus (140°C)
3290
MPa
ISO 527-1/-2
Stress at break
190
MPa
ISO 527-1/-2
Strain at break
4
%
ISO 527-1/-2
Flexural modulus
8500
MPa
ISO 178
Flexural strength
280
MPa
ISO 178
Charpy impact strength (+23°C)
70
kJ/m²
ISO 179/1eU
Charpy impact strength (-30°C)
60
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
<10
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
10
kJ/m²
ISO 180/1A
Puncture - maximum force (+23°C)
850
N
ISO 6603-2
Puncture - maximum force (-30°C)
770
N
ISO 6603-2
Puncture energy (+23°C)
2.5
J
ISO 6603-2
Puncture energy (-30°C)
2.3
J
ISO 6603-2
Thermal properties
Melting temperature (10°C/min)
260
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
230
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
250
°C
ISO 75-1/-2
Temp. of deflection under load (8.00 MPa)
90
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.8
E-4/°C
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Oxygen index
25
%
ISO 4589-1/-2
Ball pressure temperature
243
°C
IEC 60695-10-2
Glow Wire Flammability Index GWFI
650
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
2
mm
IEC 60695-2-12
Electrical properties
Relative permittivity (100Hz)
4
-
IEC 62631-2-1
Relative permittivity (1 MHz)
3.8
-
IEC 62631-2-1
Dissipation factor (100 Hz)
80
E-4
IEC 62631-2-1
Dissipation factor (1 MHz)
160
E-4
IEC 62631-2-1
Volume resistivity
1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
Ohm
IEC 62631-3-2
Electric strength
45
kV/mm
IEC 60243-1
Comparative tracking index
475
V
IEC 60112
Other properties
Water absorption
6
%
Sim. to ISO 62
Humidity absorption
2
%
Sim. to ISO 62
Density
1370
kg/m³
ISO 1183
Material specific properties
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
acc. to Karl Fischer
Melt temperature (Tmin - Tmax)
280-300
°C
Mold temperature
80-120
°C