Durethan® AKV30FN22

30% Glass Reinforced, Injection Molding, Flame Retardant (halogen free)

Back to results

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Melt volume-flow rate
17
cm³/10min
Temperature
270
°C
Load
2.16
kg
Molding shrinkage (parallel)
0.8
%
Molding shrinkage (normal)
0.9
%

Mechanical properties

Tensile modulus
6000
MPa
Stress at break
85
MPa
Strain at break
3.5
%
Flexural modulus
6700
MPa
Flexural strength
170
MPa
Charpy impact strength (+23°C)
35
kJ/m²
Charpy notched impact strength (+23°C)
<10
kJ/m²
Izod notched impact strength (+23°C)
<10
kJ/m²

Thermal properties

Melting temperature (10°C/min)
263
°C
Temp. of deflection under load (1.80 MPa)
200
°C
Temp. of deflection under load (0.45 MPa)
250
°C
Coeff. of linear therm. expansion (parallel)
0.4
E-4/°C
Coeff. of linear therm. expansion (normal)
0.8
E-4/°C
Burning Behav. at 0.75 mm nom. thickn.
V-2
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
V-2
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
V-2
class
Thickness tested
3
mm
UL recognition
Yes
-
Ball pressure temperature
255
°C
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (1) tested)
0.75
mm
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (2) tested)
1.5
mm
Glow Wire Ignition Temperature GWIT
775
°C
GWIT (Thickness (1) tested)
0.75
mm
Relative Temperature Index - electrical
115
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
95
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - without impact
125
°C
RTI without impact (Thickness (1) tested)
0.75
mm

Electrical properties

Volume resistivity
>1E13
Ohm*m
Electric strength
30
kV/mm
Comparative tracking index
525
V

Other properties

Density
1400
kg/m³

Material specific properties

Viscosity number
127
cm³/g
Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.07
%
Melt temperature (Tmin - Tmax)
260-270
°C
Mold temperature
80-100
°C