Durethan® AKV230H2.0

30% Glass Reinforced, Injection Molding, Heat Stabilized, Improved Impact

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
Regulatory Affairs
Processing technology
Injection Molding

Rheological properties

Molding shrinkage (parallel)
0.5
%
Molding shrinkage (normal)
0.85
%

Mechanical properties

Tensile modulus
8000
MPa
Stress at break
130
MPa
Strain at break
4
%
Flexural modulus
7000
MPa
Flexural strength
200
MPa
Charpy impact strength (+23°C)
75
kJ/m²
Charpy impact strength (-30°C)
85
kJ/m²
Charpy notched impact strength (+23°C)
20
kJ/m²
Charpy notched impact strength (-30°C)
15
kJ/m²
Izod notched impact strength (+23°C)
20
kJ/m²
Puncture - maximum force (+23°C)
1200
N
Puncture - maximum force (-30°C)
950
N
Puncture energy (+23°C)
7
J
Puncture energy (-30°C)
4
J

Thermal properties

Melting temperature (10°C/min)
262
°C

Other properties

Density
1300
kg/m³

Material specific properties

Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.12
%
Melt temperature (Tmin - Tmax)
280-300
°C
Mold temperature
80-120
°C