Durethan® A30SFN31

Unreinforced, Injection Molding, Flame Retardant (halogen free), Heat Stabilized, Improved flow

Back to results

General Information

Durethan® is the trade name for our range of engineering thermoplastics based on polyamide 6 and polyamide 66. These polyamides are partially crystalline thermoplastics which offer an ideal combination of properties, especially for technical applications. They provide high mechanical strength and stiffness, good dielectric properties, high resistance to both heat and chemical attack, and good friction and wear properties.
Special features
  • Good or high flow
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • CALIFORNIA PROPOSITION 65 (carbon black)2024-01-02
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • REACH Registration Statement2024-03-27
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Have a question? Contact us

Rheological properties

Molding shrinkage (parallel)
1.1
%
Molding shrinkage (normal)
1.1
%

Mechanical properties

Tensile modulus
3800
MPa
Yield stress
85
MPa
Yield strain
4.1
%
Flexural modulus
3700
MPa
Flexural strength
125
MPa
Charpy impact strength (+23°C)
60
kJ/m²
Charpy impact strength (-30°C)
50
kJ/m²
Charpy notched impact strength (+23°C)
<10
kJ/m²

Thermal properties

Melting temperature (10°C/min)
260
°C
Temp. of deflection under load (1.80 MPa)
80
°C
Temp. of deflection under load (0.45 MPa)
212
°C
Coeff. of linear therm. expansion (parallel)
0.8
E-4/°C
Coeff. of linear therm. expansion (normal)
0.7
E-4/°C
Burning Behav. at 0.4 mm nom. thickn.
V-0
class
Thickness tested
0.4
mm
Burning Behav. at 0.75 mm nom. thickn.
V-0
class
Thickness tested
0.75
mm
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
Thickness tested
3
mm
UL recognition
Yes
-
Oxygen index
34
%
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (1) tested)
0.4
mm
Glow Wire Flammability Index GWFI
960
°C
GWFI (Thickness (2) tested)
0.75
mm
Glow Wire Ignition Temperature GWIT
775
°C
GWIT (Thickness (1) tested)
0.4
mm
Glow Wire Ignition Temperature GWIT
775
°C
GWIT (Thickness (2) tested)
0.75
mm
Relative Temperature Index - electrical
130
°C
RTI electrical (Thickness (1) tested)
0.4
mm
Relative Temperature Index - with impact
105
°C
RTI with impact (Thickness (1) tested)
0.4
mm
Relative Temperature Index - without impact
125
°C
RTI without impact (Thickness (1) tested)
0.4
mm

Electrical properties

Relative permittivity (100Hz)
4
-
Relative permittivity (1 MHz)
4
-
Dissipation factor (100 Hz)
120
E-4
Dissipation factor (1 MHz)
190
E-4
Volume resistivity
1E12
Ohm*m
Surface resistivity
Ohm
Electric strength
30
kV/mm
Comparative tracking index
600
V
Inclined-Plane Tracking
1
kV

Other properties

Water absorption
7.9
%
Humidity absorption
2.6
%
Density
1170
kg/m³

Material specific properties

Drying temperature dry air dryer
80
°C
Drying time dry air dryer
2-6
h
Residual moisture content
0.03-0.07
%
Melt temperature (Tmin - Tmax)
260-270
°C
Mold temperature
80-100
°C