Rheological properties
Melt volume-flow rate
18
cm³/10min
ISO 1133
Temperature
230
°C
ISO 1133
Molding shrinkage [parallel]
1.75
%
Sim. to ISO 294-4
Molding shrinkage [normal]
2
%
Sim. to ISO 294-4
Mechanical properties
Flexural modulus
1050
MPa
ISO 178
Charpy impact strength (+23°C)
N
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
10
kJ/m²
ISO 179/1eA
Charpy notched impact strength (-30°C)
6
kJ/m²
ISO 179/1eA
Izod notched impact strength (+23°C)
9
kJ/m²
ISO 180/1A
Mechanical properties (die cutting)
Stress at break (normal)
35
MPa
ISO 527-1/-2
Strain at break (normal)
400
%
ISO 527-1/-2
Tear strength (normal)
242
kN/m
ISO 34-1; Method B
Tear strength (parallel)
242
kN/m
ISO 34-1; Method B
Thermal properties
Melting temperature (10°C/min)
221
°C
ISO 11357-1/-3
Temp. of deflection under load (0.45 MPa)
120
°C
ISO 75-1/-2
Vicat softening temperature (50°C/h 50N)
160
°C
ISO 306
Coeff. of linear therm. expansion (parallel)
1.65
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
1.65
E-4/°C
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Glow Wire Ignition Temperature GWIT
850
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
1
mm
IEC 60695-2-13
Relative Temperature Index - electrical
50
°C
UL746B
RTI electrical (Thickness (1) tested)
1.5
mm
UL746B
Relative Temperature Index - with impact
50
°C
UL746B
RTI with impact (Thickness (1) tested)
1.5
mm
UL746B
Relative Temperature Index - without impact
50
°C
UL746B
RTI without impact (Thickness (1) tested)
1.5
mm
UL746B
Electrical properties
Relative permittivity (100Hz)
3.7
-
IEC 62631-2-1
Relative permittivity (1 MHz)
3.3
-
IEC 62631-2-1
Dissipation factor (1 MHz)
300
E-4
IEC 62631-2-1
Volume resistivity
1E13
Ohm*m
IEC 62631-3-1
Electric strength
23
kV/mm
IEC 60243-1
Comparative tracking index
600
V
IEC 60112
Other properties
Water absorption
0.6
%
Sim. to ISO 62
Humidity absorption
0.15
%
Sim. to ISO 62
Density
1290
kg/m³
ISO 1183
Apparent density
830
kg/m³
ISO 60
Rheological calculation properties
Density of melt
950
kg/m³
-
Thermal conductivity of melt
0.1
W/(m K)
-
Spec. heat capacity melt
1900
J/(kg K)
-
Eff. thermal diffusivity
5.54E-8
m²/s
-
Mechanical properties (TPE)
Tensile modulus
1000
MPa
ISO 527-1/-2
Stress at 5% strain
32
MPa
ISO 527-1/-2
Stress at 10% strain
34
MPa
ISO 527-1/-2
Stress at 50% strain
25
MPa
ISO 527-1/-2
Stress at 100% strain
26
MPa
ISO 527-1/-2
Stress at break
41
MPa
ISO 527-1/-2
Strain at break
>300
%
ISO 527-1/-2
Nominal strain at break
350
%
ISO 527-1/-2
Compression Set under constant strain at 70 °C
35
%
ISO 815
Shore D Hardness (3s)
70
-
ISO 868