Melting temperature (10°C/min)
220
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
60
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
150
°C
ISO 75-1/-2
Vicat softening temperature (50°C/h 50N)
195
°C
ISO 306
Coeff. of linear therm. expansion (parallel)
0.9
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.9
E-4/°C
ISO 11359-1/-2
Burning Behav. at 1.5 mm nom. thickn.
V-2
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Burning Behav. at 3.0 mm nom. thickn.
V-2
class
IEC 60695-11-10
Thickness tested
3
mm
IEC 60695-11-10
Oxygen index
26
%
ISO 4589-1/-2
Ball pressure temperature
205
°C
IEC 60695-10-2
Glow Wire Flammability Index GWFI
900
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
1.5
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
875
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
0.75
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
825
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
1.5
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
875
°C
IEC 60695-2-13
GWIT (Thickness (2) tested)
1
mm
IEC 60695-2-13
Relative Temperature Index - electrical
130
°C
UL746B
RTI electrical (Thickness (1) tested)
0.71
mm
UL746B
Relative Temperature Index - electrical
130
°C
UL746B
RTI electrical (Thickness (2) tested)
3
mm
UL746B
Relative Temperature Index - with impact
65
°C
UL746B
RTI with impact (Thickness (1) tested)
0.71
mm
UL746B
Relative Temperature Index - with impact
70
°C
UL746B
RTI with impact (Thickness (2) tested)
3
mm
UL746B
Relative Temperature Index - without impact
85
°C
UL746B
RTI without impact (Thickness (1) tested)
0.71
mm
UL746B
Relative Temperature Index - without impact
85
°C
UL746B
RTI without impact (Thickness (2) tested)
3
mm
UL746B