IG-HG7
35% Glass Fiber Reinforced, Heat Stabilized
General Information
Special features
- Heat stabilized
General Document
Regulatory Affairs
- Absence Declaration PFAS/PFOS/PFOA/PFHxS/PFCAs2025-01-31
- Compliance Statement Sanctions and Embargos2025-11-24
- Packaging, Packaging Waste (EU) 2025/40 and CONEG declaration2025-06-24
- SVHC, REACH Annex XIV and –XVII Statement2025-11-06
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage [parallel]
0.4
%
Sim. to ISO 294-4
Molding shrinkage [normal]
1.1
%
Sim. to ISO 294-4
Mechanical properties
Tensile modulus
12000
MPa
ISO 527-1/-2
Tensile modulus (120°C)
5200
MPa
ISO 527-1/-2
Tensile modulus (150°C)
4800
MPa
ISO 527-1/-2
Tensile modulus (180°C)
4500
MPa
ISO 527-1/-2
Tensile modulus (200°C)
3800
MPa
ISO 527-1/-2
Stress at break
210
MPa
ISO 527-1/-2
Stress at break (120°C)
100
MPa
ISO 527-1/-2
Stress at break (150°C)
90
MPa
ISO 527-1/-2
Stress at break (180°C)
85
MPa
ISO 527-1/-2
Stress at break (200°C)
60
MPa
ISO 527-1/-2
Strain at break
3.2
%
ISO 527-1/-2
Strain at break (120°C)
8.5
%
ISO 527-1/-2
Strain at break (150°C)
8.8
%
ISO 527-1/-2
Strain at break (180°C)
9
%
ISO 527-1/-2
Strain at break (200°C)
9
%
ISO 527-1/-2
Flexural modulus
11300
MPa
ISO 178
Flexural strength
320
MPa
ISO 178
Charpy impact strength (+23°C)
80
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
13
kJ/m²
ISO 179/1eA
Thermal properties
Melting temperature (10°C/min)
280
°C
ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa)
255
°C
ISO 75-1/-2
Other properties
Humidity absorption
2.1
%
Sim. to ISO 62
Density
1440
kg/m³
ISO 1183