Stanyl® 46HF5145

43% Glass Reinforced, Flame Retardant, for E&E applications

Back to results

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-04-25
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2023-10-27
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-03-27
Yellow Card
Processing technology
Injection Molding
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage [parallel]
0.3
%
Molding shrinkage [normal]
0.85
%

Mechanical properties

Tensile modulus
16000
MPa
Tensile modulus (120°C)
10000
MPa
Tensile modulus (160°C)
7300
MPa
Tensile modulus, low thickness
16000
MPa
Tens. Mod. (Thickness tested)
1
mm
Stress at break
210
MPa
Stress at break (120°C)
120
MPa
Stress at break (160°C)
100
MPa
Stress at break, at low thickness
220
MPa
Stress at break (Thickness tested)
1
mm
Strain at break
1.8
%
Strain at break (120°C)
3.3
%
Strain at break (160°C)
4.5
%
Strain at break, at low thickness
1.9
%
Strain at break (Thickness tested)
1
mm
Flexural modulus
14500
MPa
Flexural modulus (120°C)
9500
MPa
Flexural modulus (160°C)
7200
MPa
Flexural strength
310
MPa
Flexural strength (120°C)
200
MPa
Flexural strength (160°C)
140
MPa
Charpy impact strength (+23°C)
50
kJ/m²
Charpy notched impact strength (+23°C)
14
kJ/m²
Izod notched impact strength (+23°C)
16
kJ/m²
Weldline strength at thickness 1
50
MPa
Weldline strain at thickness 1
0.4
%
Thickness tested (1)
4
mm
Weldline strength at thickness 2
70
MPa
Weldline strain at thickness 2
0.6
%
Thickness tested (2)
1
mm

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
280
°C
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
Thickness tested
3
mm
UL recognition
Yes
-
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (1) tested)
3
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
3
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (1) tested)
3
mm

Other properties

Humidity absorption
1.4
%
Density
1730
kg/m³

Diagrams

Applications

DDR DIMM Connectors

Industry
Electronics
Material
  • •} Sustainable solution due to good carbon footprint
  • •} Flame retardant
  • •} Halogen-free
  • •} Red-phosphorous free
}
More information

Reflow connectors (2)

Industry
Electronics
Material
PA46, PA4T excellent flow (> PEEK, PPA) PA4T low moisture absorption}