Stanyl® 46HF4550

50% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications

Back to results

General Information

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
Special features
  • Good or high flow
  • Heat stabilized
General Document
Regulatory Affairs
  • Absence Declaration BNST2023-11-16
  • Absence Declaration Biocidal Products2023-11-16
  • Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
  • Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
  • Absence Declaration EPA 20 High Priority Substances 20192023-11-16
  • Absence Declaration Food Allergens2023-11-16
  • Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
  • Absence Declaration Nano Materials2023-11-16
  • Absence Declaration Ozone Depleting Chemicals2024-06-27
  • Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
  • Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
  • Absence Declaration PFAS2024-03-05
  • Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
  • Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
  • Absence Declaration Red Phosphorus2023-11-16
  • Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
  • Compliance Statement EU Sanctions and Embargos2024-05-16
  • Conflict minerals declaration (EICC, GeSI)2024-05-15
  • Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
  • Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
  • Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
  • REACH Registration Statement2024-03-27
  • REACH STATEMENT KOREA2023-11-16
  • REACH STATEMENT TURKYE2023-11-16
  • RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
  • SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Design challenge
High Flowability
Applications
Have a question? Contact us

Rheological properties

Molding shrinkage [parallel]
0.4
%
Molding shrinkage [normal]
0.9
%
Spiral flow length 0.5mm 1200 bar
85
mm
Spiral flow length 0.5 mm 1600 bar
105
mm
Spiral flow length 0.5mm 2000 bar
115
mm

Mechanical properties

Tensile modulus
16000
MPa
Tensile modulus (120°C)
11000
MPa
Tensile modulus (160°C)
10000
MPa
Stress at break
250
MPa
Stress at break (120°C)
150
MPa
Stress at break (160°C)
135
MPa
Strain at break
2.2
%
Strain at break (120°C)
3.5
%
Strain at break (160°C)
3.5
%
Flexural modulus
15000
MPa
Flexural strength
375
MPa
Charpy impact strength (+23°C)
80
kJ/m²
Charpy impact strength (-30°C)
70
kJ/m²
Charpy notched impact strength (+23°C)
15
kJ/m²
Charpy notched impact strength (-30°C)
15
kJ/m²

Thermal properties

Melting temperature (10°C/min)
295
°C
Glass transition temperature (10°C/min)
75
°C
Temp. of deflection under load (1.80 MPa)
290
°C
Temp. of deflection under load (0.45 MPa)
290
°C
Vicat softening temperature (50°C/h 50N)
290
°C
Coeff. of linear therm. expansion (parallel)
0.1
E-4/°C
Coeff. of linear therm. expansion (normal)
1.1
E-4/°C
Coeff. of linear therm. expansion (parallel)
0.35
E-4/°C
Coeff. of linear therm. expansion (normal)
0.4
E-4/°C
Burning Behav. at 1.5 mm nom. thickn.
HB
class
Thickness tested
1.5
mm
UL recognition
Yes
-
Burning Behav. at 3.0 mm nom. thickn.
HB
class
Thickness tested
3
mm
UL recognition
Yes
-
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (1) tested)
0.75
mm
Relative Temperature Index - electrical
65
°C
RTI electrical (Thickness (2) tested)
3
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - with impact
65
°C
RTI with impact (Thickness (2) tested)
3
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (1) tested)
0.75
mm
Relative Temperature Index - without impact
65
°C
RTI without impact (Thickness (2) tested)
3
mm

Electrical properties

Relative permittivity (100Hz)
4.4
-
Relative permittivity (1 MHz)
4
-
Relative permittivity (1GHz)
3.6
-
Dissipation factor (100 Hz)
80
E-4
Dissipation factor (1 MHz)
230
E-4
Dissipation factor (1GHz)
300
E-4
Volume resistivity
1E13
Ohm*m
Surface resistivity
Ohm
Electric strength
30
kV/mm
Comparative tracking index
450
V

Other properties

Water absorption
6.75
%
Humidity absorption
1.85
%
Density
1620
kg/m³

Material specific properties

Viscosity number
75
cm³/g

Diagrams

Applications

E-Motors for Power Tools

Industry
Consumer goods
Material
  • •} Current e-motor applications are packed tight with little to no room to gain additional power or improve efficiency. With Stanyl® PA46, you can mold thinner walls (i.e., lamina stack insulation) down to .25 mm or less, allowing more room for copper windings or thicker gauge to maximize torque potential and reduce resistance.
  • •} At high loads, e-motors generate substantial heat. Temperatures can easily exceed 150°C (302°F), resulting in mechanical failures. Stanyl® PA46 offers excellent high temperature mechanical performance with a heat deflection temperature of 290°C (554°F) and a continuous use temperature of 170°C (338°F).
  • •} The superior flow and high crystallinity of Stanyl® PA46 results in strong and flexible weld lines, improving manufacturing yield by eliminating process scrap in rotors and stators.
}
More information

Reflow connectors (2)

Industry
Electronics
Material
PA46, PA4T excellent flow (> PEEK, PPA) PA4T low moisture absorption}
More information