ForTii® K11
30% Glass Reinforced, PA4T, Good Flow, Electro-friendly
General Information
ForTii® is a breakthrough high temperature polyamide with halogen-free and halogen containing flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii® in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want – and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
Product
ForTii® K11 combines excellent mechanical properties with low warpage for miniature applications such as Audio Jack and Camera Holder.
Special features
- Good or high flow
General Document
Regulatory Affairs
- Absence Declaration BNST2023-11-16
- Absence Declaration Biocidal Products2023-11-16
- Absence Declaration DMF (2009/251/EC: Dimethylfumarate)2023-11-16
- Absence Declaration ELV (2000/53/EC: Heavy metals)2024-02-15
- Absence Declaration EPA 20 High Priority Substances 20192023-11-16
- Absence Declaration Food Allergens2023-11-16
- Absence Declaration NMP (N-Methylpyrrolidone)2023-11-16
- Absence Declaration Nano Materials2023-11-16
- Absence Declaration Ozone Depleting Chemicals2024-06-27
- Absence Declaration PAH (Polycyclic Aromatic Hydrocarbons)2023-11-16
- Absence Declaration PBT chemicals under TSCA section 6(h)2023-11-16
- Absence Declaration PFAS2024-03-05
- Absence Declaration POPs (Persistent Organic Pollutants)2024-09-04
- Absence Declaration Phthalates (2005/84/EC: DEHP, DBP, BBP,DINP,DIDP, DNOP)2023-11-16
- Absence Declaration Red Phosphorus2023-11-16
- Absence Declaration opBDE (2003/11/EC: Octa- / Pentabromodiphenylether)2023-11-16
- Compliance Statement EU Sanctions and Embargos2024-05-16
- Conflict minerals declaration (EICC, GeSI)2024-05-15
- Deforestation Statement, Regulation (EU) 2023/1115 (EUDR)2024-09-19
- Packaging Declaration EU Decision 97/129/EC (labelling)2024-04-17
- Packaging, Packaging Waste and CONEG declaration (94/62/EC)2021-12-06
- REACH Registration Statement2024-03-27
- REACH STATEMENT KOREA2023-11-16
- REACH STATEMENT TURKYE2023-11-16
- RoHS Statement (2011/65/EC: Heavy metals)2024-02-01
- SVHC, REACH Annex XIV and –XVII Statement2024-11-08
Yellow Card
Processing technology
Injection Molding
Injection Molding
Rheological properties
Molding shrinkage (parallel)
0.4
%
ISO 294-4
Molding shrinkage (normal)
1.3
%
ISO 294-4
Spiral flow length 1.0 mm 1000 bar
110
mm
-
Mechanical properties
Tensile modulus
11300
MPa
ISO 527-1/-2
Tensile modulus (120°C)
8000
MPa
ISO 527-1/-2
Tensile modulus (160°C)
4500
MPa
ISO 527-1/-2
Tensile modulus (200°C)
4000
MPa
ISO 527-1/-2
Tensile modulus, low thickness
10800
MPa
ISO 527-1/-2
Tens. Mod. (Thickness tested)
1
mm
ISO 527-1/-2
Stress at break
190
MPa
ISO 527-1/-2
Stress at break (120°C)
125
MPa
ISO 527-1/-2
Stress at break (160°C)
85
MPa
ISO 527-1/-2
Stress at break (200°C)
70
MPa
ISO 527-1/-2
Stress at break, at low thickness
200
MPa
ISO 527-1/-2
Stress at break (Thickness tested)
1
mm
ISO 527-1/-2
Strain at break
2
%
ISO 527-1/-2
Strain at break (120°C)
3.5
%
ISO 527-1/-2
Strain at break (160°C)
5
%
ISO 527-1/-2
Strain at break (200°C)
5.5
%
ISO 527-1/-2
Strain at break, at low thickness
2.4
%
ISO 527-1/-2
Strain at break (Thickness tested)
1
mm
ISO 527-1/-2
Flexural modulus
10500
MPa
ISO 178
Flexural modulus (80°C)
10000
MPa
ISO 178
Flexural modulus (120°C)
7500
MPa
ISO 178
Flexural modulus (160°C)
4500
MPa
ISO 178
Flexural modulus (200°C)
4000
MPa
ISO 178
Flexural strength
290
MPa
ISO 178
Flexural strength (80°C)
250
MPa
ISO 178
Flexural strength (120°C)
180
MPa
ISO 178
Flexural strength (160°C)
120
MPa
ISO 178
Flexural strength (200°C)
100
MPa
ISO 178
Charpy impact strength (+23°C)
60
kJ/m²
ISO 179/1eU
Charpy notched impact strength (+23°C)
10
kJ/m²
ISO 179/1eA
Weldline strength at thickness 1
55
MPa
ISO 527-1/-2
Weldline strain at thickness 1
0.6
%
ISO 527-1/-2
Thickness tested (1)
4
mm
ISO 527-1/-2
Weldline strength at thickness 2
100
MPa
ISO 527-1/-2
Weldline strain at thickness 2
1.1
%
ISO 527-1/-2
Thickness tested (2)
1
mm
ISO 527-1/-2
Thermal properties
Melting temperature (10°C/min)
325
°C
ISO 11357-1/-3
Glass transition temperature (10°C/min)
125
°C
ISO 11357-1/-2
Temp. of deflection under load (1.80 MPa)
305
°C
ISO 75-1/-2
Temp. of deflection under load (0.45 MPa)
320
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.3
E-4/°C
ASTM D696
Coeff. of linear therm. expansion (normal)
0.5
E-4/°C
ASTM D696
Burning Behav. at 3.0 mm nom. thickn.
HB
class
IEC 60695-11-10
Thickness tested
3
mm
IEC 60695-11-10
UL recognition
Yes
-
-
Thermal Index 2500 hrs
185
°C
IEC 60216/ISO 527-1/-2
Thermal Index 5000 hrs
174
°C
IEC 60216/ISO 527-1/-2
Thermal Index 10000 hrs
162
°C
IEC 60216/ISO 527-1/-2
Thermal Index 20000 hrs
150
°C
IEC 60216/ISO 527-1/-2
Electrical properties
Relative permittivity (100Hz)
5
-
IEC 62631-2-1
Relative permittivity (1 MHz)
4.5
-
IEC 62631-2-1
Relative permittivity (1GHz)
3.9
-
IEC 61189-2-721
Relative permittivity (10GHz)
3.8
-
IEC 61189-2-721
Dissipation factor (100 Hz)
150
E-4
IEC 62631-2-1
Dissipation factor (1 MHz)
280
E-4
IEC 62631-2-1
Dissipation factor (1GHz)
140
E-4
IEC 61189-2-721
Dissipation factor (10GHz)
120
E-4
IEC 61189-2-721
Volume resistivity
>1E13
Ohm*m
IEC 62631-3-1
Surface resistivity
Ohm
IEC 62631-3-2
Electric strength
33
kV/mm
IEC 60243-1
Comparative tracking index
600
V
IEC 60112
Other properties
Water absorption
5.1
%
Sim. to ISO 62
Humidity absorption
2
%
Sim. to ISO 62
Density
1430
kg/m³
ISO 1183
Material specific properties
Viscosity number
98
cm³/g
ISO 307, 1157, 1628
JSON SPT
Molding shrinkage (parallel)
0.4
%
ISO 294-4
Molding shrinkage (normal)
1.3
%
ISO 294-4
Diagrams
Applications
Audio Jack Connectors
Industry
Electronics
- •} Cost-effective
- •} High flowability
- •} Low moisture absorption
- •} Flame retardant
Positition Sensor
Industry
Automotive
Material
Many different sensor types/systems: Hall-, ABS-, Oil-, MAF-, Air Bag-, Throttle- Sensor Crankshaft, Camshaft, ETC, Seat position.}
Robotic connectors & circuitry
Industry
Robotics
Material
- •} Stanyl® and ForTii® are proven solutions for connectors used by many of the world's leading automakers and electronics manufacturers.
- •} Superior strength and durability vs liquid crystal polymers (LCP) and other thermoplastics.
- •} Material solutions formulated for laser direct structuring for precision processing.
Speed Sensor
Industry
Automotive
Material
Many different sensor types/systems: Hall-, ABS-, Oil-, MAF-, Air Bag-, Throttle- Sensor Crankshaft, Camshaft, ETC, Seat position.}
Temperature Sensor
Industry
Automotive
Material
Many different sensor types/systems: Hall-, ABS-, Oil-, MAF-, Air Bag-, Throttle- Sensor Crankshaft, Camshaft, ETC, Seat position.}