Melting temperature (10°C/min)
260
°C
ISO 11357-1/-3
Glass transition temperature (10°C/min)
60
°C
ISO 11357-1/-2
Temp. of deflection under load (1.80 MPa)
247
°C
ISO 75-1/-2
Coeff. of linear therm. expansion (parallel)
0.21
E-4/°C
ISO 11359-1/-2
Coeff. of linear therm. expansion (normal)
0.67
E-4/°C
ISO 11359-1/-2
Burning Behav. at 0.75 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
0.75
mm
IEC 60695-11-10
Burning Behav. at 1.5 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
Burning Behav. at 3.0 mm nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
3
mm
IEC 60695-11-10
Ball pressure temperature
255
°C
IEC 60695-10-2
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (1) tested)
0.4
mm
IEC 60695-2-12
Glow Wire Flammability Index GWFI
960
°C
IEC 60695-2-12
GWFI (Thickness (2) tested)
3
mm
IEC 60695-2-12
Glow Wire Ignition Temperature GWIT
800
°C
IEC 60695-2-13
GWIT (Thickness (1) tested)
0.4
mm
IEC 60695-2-13
Glow Wire Ignition Temperature GWIT
825
°C
IEC 60695-2-13
GWIT (Thickness (2) tested)
3
mm
IEC 60695-2-13
Relative Temperature Index - electrical
125
°C
UL746B
RTI electrical (Thickness (1) tested)
0.75
mm
UL746B
Relative Temperature Index - electrical
125
°C
UL746B
RTI electrical (Thickness (2) tested)
3
mm
UL746B
Relative Temperature Index - with impact
105
°C
UL746B
RTI with impact (Thickness (1) tested)
0.75
mm
UL746B
Relative Temperature Index - with impact
105
°C
UL746B
RTI with impact (Thickness (2) tested)
3
mm
UL746B
Relative Temperature Index - without impact
115
°C
UL746B
RTI without impact (Thickness (1) tested)
0.75
mm
UL746B
Relative Temperature Index - without impact
115
°C
UL746B
RTI without impact (Thickness (2) tested)
3
mm
UL746B